Popular articles

How can crevice corrosion be reduced?

How can crevice corrosion be reduced?

Use butt weld joints instead of bolted or threaded joints for new equipment. Use continuous welding or soldering to eliminate crevices in lap joints. Ensure complete vessel drainage where possible and design any non-draining areas to allow sufficient solution flow to prevent stagnation.

How do you find corrosion in crevice?

Crevice corrosion is sometimes observed at the interface between water and air (or other gas) in storage tanks and pressure vessels. The area just above this line is often freely exposed to oxygen while the area just below the line will see much less.

What is essential crevice corrosion?

Oxygen is essential for the formation of passive film on the metal surface. Hence, it has an important influence on the onset of crevice corrosion. As oxygen is consumed within the crevice, a potential difference is set up between the creviced areas and the boldly exposed areas open to oxygen.

What is the most common corrosion found on aluminum?

Galvanic and Pitting Corrosion Are the Most Common Corrosion Types for Aluminum Surfaces. Galvanic corrosion and pitting corrosion are the biggest culprits when it comes to corrosion-related deterioration of aluminum.

What is the difference between pitting and crevice corrosion?

Whereas pitting corrosion occurs across the surface of a component, crevice corrosion is associated with a crevice, be that one that forms around a fastener, washer or joint, in a sharp corner or in an area where the flow of a liquid is slowed i.e. a dead spot.

What is the difference between crevice corrosion and pitting corrosion?

How do you fix aluminum corrosion?

Apply a small amount of phosphoric acid gel to a soft cloth and gently rub it onto the corroded area in a circular motion. Allow the gel to sit on the area for about 10 minutes. Wipe it off with a dry cloth, but do not continue to rub it in.

How do you stop aluminum corrosion?

Painting, anodizing or any surface treatment that forms a coating on the aluminium surface will protect the surface from pitting attack. In applications when you want to preserve the aluminium look and still have a surface resistant to pitting, a clear coat or thin anodic coating would be suitable surface treatments.

How do you fix pitting corrosion?

Another viable method for repairing pitting corrosion is the use of cold-applied epoxy materials. These 100% solids, paste-grade materials have been on the market since the 1960s and have been continuously improved to withstand greater temperatures and pressure levels as well as various in-service conditions.

How does corrosion fatigue take place in aluminium?

Corrosion fatigue in aluminium occurs when it is repeatedly subjected to low stress for long periods of time. The crack initiation and propagation takes place with greater ease in a corrosive environment like seawater and salt solutions. Corrosion fatigue cannot proceed without the presence of water in the atmosphere.

Are there different types of corrosion in aluminium?

There are multiple variations of intergranular corrosion based on thermochemical treatments and metallic structures. It is also found to different degrees in different series of aluminium alloys. The 6xxx series alloys, for instance, are relatively less susceptible to this type of aluminium corrosion.

Where does exfoliation corrosion occur in an aluminium alloy?

Exfoliation corrosion is a special type of intergranular corrosion found in aluminium alloys that have marked directional structures. This is predominantly evident in aluminium products that have undergone hot or cold rolling processes. It occurs along elongated grain boundaries in the microstructure.

What kind of corrosion occurs in a crevice?

Crevice corrosion (CC) is a form of localized corrosion that occurs within crevices and other shielded areas where a small volume of a stagnant solution is present.